Synthetic Magnesia Olivine Brick
- Apparent Porosity :20 ％
- Bulk Density :2.7 g/cm3
- Cold Crushing Strength :35 Mpa
- 0.2Mpa Refractoriness Under Load T0.6:1650
Description
Specification:
Synthetic magnesia olivine brick is neutral refractories with sintered olivine , serpentine and periclase as main phase .It has better alkaline slag leaching resistance.
Application:
It is a kind of environmentally friendly product and a substitute for magnesia chrome brick used in glass furnace .The product has been successfully used in glass kilns at home and abroad for many years.
Synthetic magnesia olivine brick is neutral refractories with sintered olivine , serpentine and periclase as main phase .It has better alkaline slag leaching resistance.
Application:
It is a kind of environmentally friendly product and a substitute for magnesia chrome brick used in glass furnace .The product has been successfully used in glass kilns at home and abroad for many years.
Specification
| Item | Behaviors | ||
| Synthetic Magnesia Olivine Brick | |||
| TY-MO-60 | TY-MO-50 | ||
| Chemical composition | MgO ％ | 60 | 50 |
| SiO2 ％ | 20 | 30 | |
| Apparent Porosity ％ | 20 | 20 | |
| Bulk Density g/cm3 | 2.7 | 2.65 | |
| Cold Crushing Strength Mpa | 35 | 35 | |
| 0.2Mpa Refractoriness Under Load T0.6 | 1650 | 1620 | |
| Thermal shock resistance(950℃ air cooling ,times) | 10 | 10 | |