Magnesia Zirconia Brick
- Apparent Porosity:≤19 %
- Bulk Density :≥3.95 (g/cm3)
- Cold Crushing Strength :≥50 (MPa)
- Refractoriness Under Load:≥1600 °C
Description
Specifications:
♦ alkali resistance
♦ slag corrosion resistance
♦ spalling resistance
♦ high-temperature resistance
Descriptions:
The product is composed of fused magnesia sand and zircon sand and it belongs to alkaline material. This product has high density (Bulk density) is greater than 3.08g/cm3).It also resists alkaline atmosphere erosion and alkaline slag erosion and widely used in glass furnace, regenerative chamber, cement kiln, steel-making electric furnace and non-ferrous metal metallurgy.
Application:
Magnesia Zircon Brick is used for regenerator of glass furnace.
♦ alkali resistance
♦ slag corrosion resistance
♦ spalling resistance
♦ high-temperature resistance
Descriptions:
The product is composed of fused magnesia sand and zircon sand and it belongs to alkaline material. This product has high density (Bulk density) is greater than 3.08g/cm3).It also resists alkaline atmosphere erosion and alkaline slag erosion and widely used in glass furnace, regenerative chamber, cement kiln, steel-making electric furnace and non-ferrous metal metallurgy.
Application:
Magnesia Zircon Brick is used for regenerator of glass furnace.
Specification
|
Item |
Magnesia Zircon Brick |
||
|
TY-MZ8 |
TY-MZ10 |
TY-MZ13 |
|
|
MgO% ≥ |
80 |
75 |
70 |
|
ZrO2 %≥ |
8 |
10 |
13 |
|
Apparent Porosity%≤ |
19 |
18 |
18 |
|
Bulk Density (g/cm3)≥ |
3.95 |
3.00 |
3.05 |
|
Cold Crushing Strength (MPa)≥ |
50 |
45 |
40 |
|
Refractoriness Under Load°C≥ |
1600 |
1550 |
1600 |
|
Thermal Shock Resistance(950-wind cold)≥ |
10 |
10 |
10 |